A chill can be as simple as a steel plate/block of sufficient size to **** the heat right out of an area quickly. One would just spray some graphite or whatnot carbon on it, and it'll keep it from sticking to the casting. Chill practice is a bit of an art. Later on they would use Chromite or...

Nodular is not what you're describing, at all. It's marginally harder, but machines more like a steel with less powdery and more stringy chips. One old name for it is "semi-steel". There are nodular irons with machinability indices from 70 all the way up to 140, so in general, they are very...

To determine if it's nodular for sure, you'd need a sample which can be polished / etched and micrographs taken to look for graphite flakes vs graphite spheres. I don't think you can do it nondestructively and get anything more than "we think," LOL.

You're thinking the right way. The insert piece has to have a gap around it so that the cast metal can flow around it and carry heat in there. Ideally, one would put a "lump" around this area and then later machine it off. That would make sure you have plenty of hot metal flowing around the...

To be more clear, I wouldn't use the term "geometric transition," I'd use the words "abrupt change in section thickness." You can have smooth flowing transitions that handle load well, but square corners involving abruptly necked-down sections are notorious.

Cool...I wasn't aware if USPTO had records >100 years old.

Metallurgist here. You are correct that the wrought iron / steel has a higher melting point, and if thick enough, they will stay in there and provide strength in tension, which is exactly what cast iron ***** at. If the steel is very fine, like a wire, and you are pouring a lot of metal past...

Hi guys, been a long time since I posted but I only post when I find a cool vise, and I have been skunked for several years finding a noteworthy one. Then this morning...I actually completed a FB Marketplace transaction :LOL: Lick your chops...7" Williamson :love: I've only ever seen a few...

This heater is several years old and started doing this. It produces heat and doesn't stink, but the popping is driving me nuts. When it's cold, sometimes the popping blows the flame out and the thing can't be trusted to start (it has a thermostat which is handy for unattended operation). Took...

No....where was it listed?

Nice Prentiss 58 just ended on fleaBay at $1663. Yowza.

^^^ That's a classy vise.

Ya got me.....dang rookies always a step behind :bowdown:

Emmert 10A triple jaw swivelrama special on eBay for a cool $3850!!! Somebody lay down some paychecks!! :D Seller says "WE HAVE HERE A VERY, VERY, VERY, VERY, VERY, DID I SAY VERY RARE EMMERT 10A" "HERE IS THE CHANCE TO GET ONE OF THE MOST RAREST OF VISES ON THE PLANET !!!!!!!!"

Yeah, I hear ya, but I am kinda OCD about checking CL daily....guess I'll have to stay on here more so the other inmates can steer me to where I can get my next hit :D $1k was probably out of reach for me at the moment anyway...buying go-fast parts for my truck is killing my free cash flow...

Ah fiddle faddle.....:headshake I guess I need to up my game....

Thanks everyone....but did that 109 come out of Pittsburgh? Please tell me it wasn't a Craigslist miss..... Can't be upset if Demoman got it.....went to the hall of fame collection :D

Guilty as charged. Where was this Reed 109 sighting? I got a buddy who would saw his arm off for one. His family worked at Reed. If there's a link to it, I'd love to see it.

That's pretty cool, never heard of Jacobson.

Yeah, CL is full of idiots and liars. There was a decent sized vise here in the Pittsburgh area that obviously had the support "shelf" (or whatever you call the extension of the base that helps support the moving jaw) broken off and re-brazed back on. The guy must have got called on it because...